What Is Alloy steel F5 Rods?
Alloy Steel F5 Rods are commercially pure wrought Nickel with similar properties but with lower carbon content to prevent embrittlement by inter-granular carbon at elevated temperatures. These Alloy Steel F5 Bars are highly acknowledged and commended in this industry, along with resistance to seawater and steam at high temperatures.
Alloy Steel F5 Rods show high strength and excellent corrosion resistance in a range of acidic and alkaline environments and it’s especially suitable for reducing conditions. Alloy Steel F5 Rods have corrosion resistance in an extensive range of marine and chemical environments – from pure water to non-oxidizing mineral acids, salts, and alkalis.
Specification of Alloy Steel F5 Rods
Dimensions: ASTM, ASME, DIN, BS, EN, IS, AMS, JIS, IBR & Other
International Standards.
Standard: ASTM A182 / ASME SA182
Range: 5mm to 500mm dia in 100mm to 6000mm Length
Diameter: 10 mm To 200 mm
Thickness: 0.5mm to 500mm Diameter
High-Speed Steel (HSS), HCHCR & OHNS in Grade:M2, M3, M35, M42, T-1, T-4, T-15, T-42, D2, D3, H11, H13, OHNS-01 & EN52
Finish: Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish
Length: 1000 mm Long To 6000 mm Long
Form: Round, Square, Hex, Flat, Rectangular, Forged, Rod, etc.
Equivalent Standard Grade Of Alloy Steel F5 Rods
STANDARD – ASTM A182 F5, WERKSTOFF NR. – 1.7362, UNS – K41545
EN – 5Cr-1/2Mo, DIN – 12CRMO195
Chemical Composition of F5 Rods
Grade | C | Mn | Si | P | S | Cr | Mo |
Alloy Steel F5 | 0.15 max | 0.3-0.6 | 0.5 | 0.03 | 0.03 | 4-6 | 0.44-0.65 |
Mechanical Properties of F5 Rods
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min |
A182 F5 | 275 | 485 | 20 |